Stainless Steel Can Be Heat-Treated to 50-53 HRC
International Mold Steel will introduce S-Star-A, a 420 stainless steel in the annealed condition that can be heat-treated to hardness of 50-53 HRC and will be stocked in plate form to 6" thick.
International Mold Steel will introduce S-Star-A, a 420 stainless steel in the annealed condition that can be heat-treated to hardness of 50-53 HRC and will be stocked in plate form to 6" thick. S-Star-PH is a prehardened (30/34 HRC) 420 stainless steel that can also be heated to 50-53 HRC and will be stocked in round bar ranging to 4" in diameter.
The company has also added new processing capabilities, including a large plate saw that can cut to 24" thickness, side milling to 31.5" square and gun drilling to 1 ¾" in diameter by 84" long.
Related Content
-
How to Reduce Cycle Times by 70% and More on Your Existing CNCs and Dramatically Improve Tool Life Too
By employing advanced high efficiency milling techniques for the entire machining routine, SolidCAM’s iMachining technology can drastically reduce cycle times while vastly improving tool life compared to traditional milling.
-
Palmgren Launches Combination Bench Lathe, Mill
The 11" bench engine lathe and gear head mill is able to handle a wide range of turning, milling and drilling operations typically found on much larger machinery.
-
A New Milling 101: Milling Forces and Formulas
The forces involved in the milling process can be quantified, thus allowing mathematical tools to predict and control these forces. Formulas for calculating these forces accurately make it possible to optimize the quality of milling operations.